Beilstein J. Nanotechnol. 2018, 9, 1040–1049, doi:10.3762/bjnano.9.97
Figure 1: (a) Cosine of 18 times the magnetic phase shift recorded using EH from Co NWs deposited at electron...
Figure 2: (a) In-focus bright-field TEM image of a Co NW. (b) L-TEM underfocus image of the NW, exhibiting a ...
Figure 3: L-TEM images of square rings, showing the magnetization directions under different magnetic fields B...
Figure 4: (a) AFM image of a square ring. (b) Height profile corresponding to the red dashed line in (a). (c)...
Beilstein J. Nanotechnol. 2015, 6, 1298–1305, doi:10.3762/bjnano.6.134
Figure 1: (a) SEM image (at 52° tilt angle) of suspended nanowire (SNW) 1 deposited between pillars; (b) elec...
Figure 2: (a) Current(I)–voltage(V) measurements on SNW 1. In the inset, the first I–V measurement taken on t...
Figure 3: Bright-field TEM image of SNW 1 after electrical measurements. In the inset, the SAED pattern taken...
Figure 4: (a) SEM image (at 20° tilt angle) of SNW 2 deposited between the Au pads across the slit. (b) Five ...
Figure 5: Bright-field TEM image of SNW 2 as shown in Figure 4c. In the top inset, the SAED pattern taken on the blue-...
Figure 6: (a) SEM image (at 52° tilt angle) of SNW 3 deposited between Au pads; (b) Three subsequent I–V meas...